SAE ARP4462 Barkhausen Noise Inspection for Detecting Grinding Burns in High Strength Steel Parts
作者:标准资料网 时间:2024-05-07 19:46:20 浏览:9578
来源:标准资料网
下载地址: 点击此处下载
Product Code:SAE ARP4462
Title:Barkhausen Noise Inspection for Detecting Grinding Burns in High Strength Steel Parts
Issuing Committee:Ams K Non Destructive Methods And Processes Committee
Scope: This recommended practice covers the procedures and method for establishing acceptance criteria when performing Barkhausen noise testing of surface-hardened steel components to detect grinding burns (metallurgical damage caused by over-heating) in bare or chromium-plated parts. Primarily for nondestructive testing of heat treated, high strength low-alloy steel parts which have been ground, in accordance with MIL-STD-866 or commercial standard, before or after chromium plating. This test method may be used as an independent test or to confirm grinding damage detected in accordance with AMS 2440 or MIL-STD-867 in bare or chromium plated components.
Rationale: This recommended practice covers the procedures and method for establishing acceptance criteria when performing Barkhausen noise testing of surface-hardened steel components to detect grinding burns (metallurgical damage caused by over-heating) in bare or chromium-plated parts. Primarily for nondestructive testing of heat treated, high strength low-alloy steel parts which have been ground, in accordance with MIL-STD-866 or commercial standard, before or after chromium plating. This test method may be used as an independent test or to confirm grinding damage detected in accordance with AMS 2440 or MIL-STD-867 in bare or chromium plated components.
Title:Barkhausen Noise Inspection for Detecting Grinding Burns in High Strength Steel Parts
Issuing Committee:Ams K Non Destructive Methods And Processes Committee
Scope: This recommended practice covers the procedures and method for establishing acceptance criteria when performing Barkhausen noise testing of surface-hardened steel components to detect grinding burns (metallurgical damage caused by over-heating) in bare or chromium-plated parts. Primarily for nondestructive testing of heat treated, high strength low-alloy steel parts which have been ground, in accordance with MIL-STD-866 or commercial standard, before or after chromium plating. This test method may be used as an independent test or to confirm grinding damage detected in accordance with AMS 2440 or MIL-STD-867 in bare or chromium plated components.
Rationale: This recommended practice covers the procedures and method for establishing acceptance criteria when performing Barkhausen noise testing of surface-hardened steel components to detect grinding burns (metallurgical damage caused by over-heating) in bare or chromium-plated parts. Primarily for nondestructive testing of heat treated, high strength low-alloy steel parts which have been ground, in accordance with MIL-STD-866 or commercial standard, before or after chromium plating. This test method may be used as an independent test or to confirm grinding damage detected in accordance with AMS 2440 or MIL-STD-867 in bare or chromium plated components.